Fe75-xCoxCu1Nb3Si15B6 Alloy with Rapid Stress Annealing IJTSRD


This Articler reports the effect of stress annealing treatment on the structural and magnetic properties of nanocrystalline Fe75-xCoxCu1Nb3Si15B6 & Co21Fe64-xNbxB15 alloys. Information obtained from magnetic measurements, X-ray diffraction measurements and Mössbauer spectroscopy reveal that for Fe75-xCoxCu1Nb3Si15B6 (x = 0, 2, 5) alloys the volume fraction of the Fe-Co nanograins and their grain diameter ranges between 56 to 80 % and 10 to 18 nm respectively. Annealing treatment at higher temperature also resulted in appearance of Fe3Si nanocrystals along with magnetically hard Fe3B, Fe23B type phases which are responsible for higher coercive field values. Presence of cobalt and applied stress during annealing has considerable effect on relative permeability and stress induced anisotropy, which is and perpendicular to the ribbon axis. Mössbauer spectroscopy analysis also suggests changes in spin texture.

Shailendra Singh Khinchi”Fe75-xCoxCu1Nb3Si15B6 Alloy with Rapid Stress Annealing”

Published in International Journal of Trend in Scientific Research and Development (ijtsrd), ISSN: 2456-6470, Volume-1 | Issue-5 , August 2017,

URL: http://www.ijtsrd.com/papers/ijtsrd2272.pdf

http://www.ijtsrd.com/physics/engineering-physics/2272/fe75-xcoxcu1nb3si15b6-alloy-with-rapid-stress-annealing/shailendra-singh-khinchi

call for paper Mechanical Engineering, international journal Structural Engineering, ugc approved journals Engineering




Fe75-xCoxCu1Nb3Si15B6 Alloy with Rapid Stress Annealing IJTSRD IEEE PAPER





2020 technology trends
2019-TOP-TECHNOLOGIES
2019 papers
2018-TOP-TECHNOLOGIES
2018 papers

IEEE PROJECTS 2019


IEEE PROJECTS CSE 2019
IEEE PROJECTS ECE 2019
IEEE PROJECTS EEE 2019
IEEE PROJECTS VLSI
IEEE PROJECTS EMBEDDED SYSTEM

IEEE PROJECTS


IEEE PROJECTS ECE
IEEE PROJECTS CSE COMPUTER SCIENCE
IEEE PROJECTS ELECTRICAL ENGINEERING
IEEE PROJECTS EEE

IEEE PROJECTS